(Department of Science, Faculty of Science and Agricultural Technology, Rajamangala University of Technology Lanna, Lampang, 52000, Thailand)
Description
In this research, ceramics fly-ash doped kaolin 10 to 50 wt.% were fabricated by solid-state reaction. All powders were weighed, mixed and further milled by ball-milling for 4 h. All compositions of powders were uniaxial pressed in pellets and sintered at the temperatures 1100 $^{\circ}$C for 4 h. Compositions of the ceramics were investigated by using X-ray diffraction technique. The particle size of powder and microstructure of ceramics were measured by scanning electron microscope. The result shows relationships between ratio of fly-ash doped kaolin with mechanical properties and heat-insulating of ceramics.
Author
Dr
Narit Funsueb
(Department of Science, Faculty of Science and Agricultural Technology, Rajamangala University of Technology Lanna, Lampang, 52000, Thailand)
Co-authors
Mr
Watee Panthuwat
(Department of Science, Faculty of Science and Agricultural Technology, Rajamangala University of Technology Lanna, Lampang, 52000, Thailand)
Mr
Anawin Thipboonraj
(Department of Industrial Engineering, Faculty of Engineering, Rajamangala University of Technology Lanna, Lampang, 52000, Thailand)
Dr
Pat Pranamornkith
(Department of Science, Faculty of Science and Agricultural Technology, Rajamangala University of Technology Lanna, Lampang, 52000, Thailand)